Title:
Preparation and Property Analysis of a FerroelectricSuperlattice
文章编号:
1673-4432(2017)05-0057-04
作者:
黄奇辉12
(1.厦门理工学院光电与通信工程学院,福建 厦门 361024;〖JZ〗2.福建省光电技术与器件重点实验室,福建 厦门 361024)
Author(s):
HUANG Qihui〖MZ)〗12
(1.School of Optoelectronics & Communication Engineering,Xiamen University of Technology,Xiamen 361024,China;2.Fujian Key Laboratory of Optoelectronic Technology and Devices,Xiamen 361024,China)
关键词:
铁电超晶格PZT铁电薄膜LNO薄膜磁控溅射
Keywords:
ferroelectric superlatticePZT ferroelectric thin filmLNO thin filmmagnetron sputtering
分类号:
TB32
DOI:
-
文献标志码:
A
摘要:
采用射频磁控溅射工艺,制备了三周期铁电超晶格[PZT/LNO]3/Si。对周期结构样品的结晶取向、表面形貌、电滞回线、反射光谱、膜厚等特性的一系列测试分析显示,制备的样品表面较平整,颗粒尺寸均很小,晶格匹配可以诱导择优取向,铁电性能优于单层膜;对光产生了干涉效应,可作为信息存储与传播材料,亦可应用于非制冷红外焦平面器件。
Abstract:
A three period Ferroelectric Superlattice ([PZT/LNO]3/Si) has been prepared by RF magnetron sputtering.A series of tests and analyses on the crystalline orientation,surface morphology,hysteresis loop,reflection spectrum and film thickness of its periodic structure sample show that the prepared sample has smooth surface and tiny particles,its lattice matching is capable to induce preferential orientation,its multilayer films carry better ferroelectric properties than those of single layer films,and it produces interference effect on light that makes it useful as information storage and propagation materials and for uncooled infrared focal plane devices.

参考文献/References:

[1]〖ZK(〗ZHAO Xuelian,JIANG Dan,YU Shengwen,et al.Structure and electrical properties of PZT/LNO/PT multilayer films on stainless steel substrates[J].Rare Metals,2012,31(3):272.〖ZK)〗[2]〖ZK(〗NAKHMANSON S M,RABE K M,DAVID V.Predicting polarization enhancement in multicomponent ferroelectric superlattices[J].Phys Rev,2006,73(38):060101〖ZK)〗[3]〖ZK(〗王英龙,刘林,张鹏程,等.薄膜厚度对PZT/STO铁电电容器遂川电阻的影响[J].功能材料,2013,44(3):363370.〖ZK)〗[4]〖ZK(〗高龙,杨世源,王进,等.多孔PZT95/5铁电陶瓷的孔隙率与点电性能[J].人工晶体学报,2013,42(3):446451.〖ZK)〗[5]〖ZK(〗胡古今.高反射率周期性铁电多层膜形成机理研究[J].红外与毫米波学报,2007,26(2):8991.〖ZK)〗[6]〖ZK(〗朱斌,文忠,高扬.铟掺杂PZT铁电陶瓷性能研究[J].功能材料,2013,44(5):614617.〖ZK)〗[7]〖ZK(〗包定华,阮凯斌.铁电多层膜与铁电超晶格[J].四川大学学报(自然科学版),2005,42(增刊2):3135.〖ZK)〗〖HT〗

相似文献/References:

备注/Memo

备注/Memo:
[收稿日期]2017-05-03〓〓〓〓[修回日期]2017-06-07〖HTH〗[基金项目]〖HTSS〗〖ZK(〗厦门市对台科技合作与交流基地项目(3502Z20141042) ;厦门理工学院教育教学改革与建设项目(JGY201621);厦门理工学院对外科技合作专项(E201401600)〖ZK)〗〖HTH〗[作者简介]〖HTSS〗黄奇辉(1982-),男,实验师,硕士,研究方向为光电子材料,〖BF〗Email:qhhuang@xmut.edu.cn〖BFQ〗。
更新日期/Last Update: