[1]牛海侠,朱松波,张琼,等.液态模锻成形的2A14履带板性能分析[J].厦门理工学院学报,2020,(5):73-80.[doi:1019697/jcnki16734432202005012]
　NIU Haixia,ZHU Songbo,ZHANG Qiong,et al.Performance of Liquid Die Forged 2A14 Track Plate[J].Journal of JOURNAL OF XIAMEN,2020,(5):73-80.[doi:1019697/jcnki16734432202005012]
点击复制

液态模锻成形的2A14履带板性能分析(PDF/HTML)
分享到：

《厦门理工学院学报》[ISSN:1673-4432/CN:35-1289/Z]

卷:
期数:
2020年第5期
页码:
73-80
栏目:
材料科学与工程
出版日期:
2020-10-30

文章信息/Info

Title:
Performance of Liquid Die Forged 2A14 Track Plate
文章编号:
16734432(2020)05007308
作者:
牛海侠1; 朱松波2; 张琼1; 吴建美1
（1 安徽三联学院机械工程学院，安徽 合肥 230601； 2 天津津航计算技术研究所，天津 300300)
Author(s):
NIU Haixia1; ZHU Songbo2; ZHANG Qiong1; WU Jianmei1
(1.School of Mechanical Engineering,Anhui Sanlian University,Hefei 230601,China 2.Tianjin Jinhang Institute of Computing Technology,Tianjin 300300,China)
关键词:
铝合金履带板; 2A14履带板; 液态模锻成形; 性能分析; 热处理
Keywords:
aluminum alloy track plate2A14 track plateliquid die forgingperformance analysisheat treatment
分类号:
TG1463
DOI:
1019697/jcnki16734432202005012
文献标志码:
A
摘要:
采用液态模锻成形工艺，成形出某特种车辆2A14履带板；然后分析其金相组织，测试其耐磨性、力学性能和凸起部位的硬度。结果显示，经过热处理后，强化相大量弥散分布在晶粒内部和晶界之间，质点产生晶格畸变，履带板强度和硬度明显提高，抗拉强度提高602%，屈服强度提高626%；沿水平中心线正方向，履带板凸起部位的硬度值越来越大，并呈规律分布；履带板主要受到磨粒磨损，并伴有少量粘着磨损。研究表明，液态模锻成形的2A14履带板性能较好，热处理工艺能够显著提高零件综合性能。
Abstract:
A special vehicle 2A14 track plate was formed by liquid die forging forming process.The microstructure was observed and the wear resistance,mechanical properties and the hardness of the protruding part were tested.Experimental results show that,after heat treatment,a large number of strengthening phases are dispersed in the interior of grains and between grain boundaries,resulting in lattice distortion of particles,and remarkably improved strength and hardness of track plate at a 76.8% increase of the tensile strength and a 62.6% increase of the yield strength.In addition,the protruded part of the track plate shows regularly distributed hardness increasing in the positive direction of the horizontal centerline,and mainly abrasive wear accompanied by a small amount of adhesive wear.The results show that the performance of the 2A14 track plate is good,and the heat treatment process can improve the comprehensive performance of the parts significantly.

参考文献/References:

［1］ 刘勇涛,徐胜良,王思涛,等.2A50负重轮液态模锻模具使用寿命分析及模具改进［J］.新技术新工艺,2019(7):810. ［2］ 李顺,李宏伟,张新,等.高性能铝合金结构件液态模锻技术研究材料与热处理［J］.新技术新工艺,2015(6):129134. ［3］ 洪慎章,曾振鹏.铝合金零件半固态模锻的应用及发展［J］.锻压技术,2004(4):57. ［4］ 刘劲松,王惠敏.半固态模锻及其工业应用前景展望［J］.模具制造,2004(3):4749. ［5］ CHOU H N,GOVENDER G,LVANCHEV L.Opportunities and challenges for use of SSM forming in the aerospace industry［J］.Solid State Phenomena,2006,116117:9295. ［6］ 李艳,于克杰,李小雷.铆钉材料对铆接变形影响的有限元分析［J］.机床与液压,2013,41(4):5052. ［7］ 刘静安.铝合金锻压生产现状及锻件应用前景分析［J］.铝加工,2005(2):59. ［8］ 李文刚.铝合金薄壁零件的机械加工工艺研究［J］.军民两用技术与产品,2018(14):119130． ［9］ 徐慧,李天生.铝合金的液态模锻成形［J］.机械工程师,2006(11):6971. ［10］ 徐胜利.臂板件液态模锻分析与模具设计［J］.锻压装备与制造技术,2019(4):97100. ［11］ 张屹林,闫汝辉,王秀金.铝活塞液态模锻常见缺陷分析［J］.铸造技术,2006(27):1 3601 362.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期：20200515修回日期：20201011 基金项目：安徽省教育厅高校自然科学重点项目（KJ2019A0892）；安徽省高校优秀拔尖人才培育资助项目（gxgnfx2019071）；安徽三联学院科研基金重点课题（KJZD2020004） 通信作者：牛海侠，女，副教授，硕士，研究方向为铝合金成形技术、材料加工工程，Email：niuhaixia2005@126.com。
更新日期/Last Update: